Testing results, a wide scope of test assures a better structuarally engineered support system Advanced Support Products Inc, the industry leader in pipe and equipment support systems

Recycled Rubber MSDS Sheet

Download
Download

Molded Recycled Tire Compound (Post Industrial)

Composition Recycled Rubber Tires - 100% Virgin Rubber Compound
Cable TrayThickness/Weight 3" /8.0 lbs./sq. ft.
Walk Pad Thickness/Weight 1/2" /3.0 lbs./sq. ft.
Curb Supports Thickness/Weight 4" /8.0 lbs./lf.
Surfaces Flat Anti-Skid Surface
Color Black
Tensile Strength ASTM D412-92 1000 psi
Hardness ASTM D2240-91 60 Shore A
Flammability Meets Federal Flammability Standard Doc FF 1-70 CPSC
Dimensional Stability +0.242% at two hours @ 60ºC
-0.092% at 48 hours @ 20ºC & 65% Rel. Humidity
Ultimate Elongation ASTM D412-87 152%
Flame Spread (UL 94 Standard, Horizontal Burning test for Classifying Material 94HB) 0.495"/Min on 3/4" thick mat
Critical Radiant Flux ASTM E648-94a 0.11 watts/sq. cm
Electrical Resistance ASTM D991 1.6 x 10 9 megohms average
5.6 x 10 8 megohms average
Electrostatic Propensity AATCC Test Method 134-1991 NEG 0.9 KV Maximum Voltage
Thermal Resistance R-Value 0.36 per 1/2"
Thermal Resistivity   .72 (all thicknesses)
Thermal Conductance   2.78 per 1/2" - 1.78 per 3/4"
Thermal Conductivity K-Value 1.39 (all thicknesses)
Tear Resistance (ppi) ASTM D624-91 122 lbs./in.
Coefficient of Friction ASTM D1894 0.96
Density (lb/ft3) ASTM D3676 1039 Relatively Dense
Oil/Gasoline ASTM D2240-95 No Effect
Salt ASTM B117-95 No Effect
UV Aging ASTM G23-88 No Cracks or Deterioration
Compression & Recovery ASTM D575 Immediate 98.1%
After 24 hours 99.2%
After 48 hours 99.4%
After 72 hours 99.7%
After 96 hours 99.7%
Accelerated Weathering
Carbon Arch Weather-ometer		 Fed-Std-191 Method 5804 except with filters removed Tensile psi Elongation, %
Unexposed 499 145
Full Exposure 344 70